Art Clay Paste
650/1200 Low Fire Overlay Silver Paste 15g
Art Clay Silver 650/1200 Overlay Silver Paste (OSP) is "low-fire" silver clay in paste form, formulated specifically to use on glazed porcelain. We use Overlay Paste in stead of OIL PASTE as we find it is more effective & then YOU have one less product to buy ^_^
More info...
Art Clay Silver 650/1200 Overlay Silver Paste (OSP) is "low-fire" silver clay in paste form, formulated specifically to use on glazed porcelain. Overlay Silver Paste is in a viscous, liquid form and water soluble, so that you can express 3 dimensional drawings on a surface of porcelain, ceramic or glass.
After firing at appropriate temperature ranging from 650 ºC/1200 ºF to 800 ºC/1472 ºF, it will turn into 99.9% silver. During firing, the pure silver powder solidifies. The binding agent consists of carbon, hydrogen and oxygen resulting in the release of harmless carbon dioxide and steam during firing. [Instructions] Some silver settling may occur at bottom of the jar. Stir the paste well with a brush or metal spatula before use.
This product is water-based and can dry. Always keep the container tightly capped. If it dries, add a small amount of water to re-hydrate. To dilute the paste, take out the necessary amount and place it in a separate container. Then, add water a drop at a time. Do not dilute it directly in the bottle. It is important that your kiln €™s pyrometer is functioning properly. Always be sure to ventilate the workroom when using a kiln.
650/1200 Low Fire Silver Paste 10g
Art Clay Silver 650/1200 Paste consists of pure silver particles, a binding agent and water.
Art Clay Silver 650/1200 Paste consists of pure silver particles, a binding agent and water. The binding agent is produced from harmless pulp fiber. During firing, the pure silver particles solidify. The binding agent consists of carbon, hydrogen, and oxygen resulting in the release of harmless carbon dioxide and steam during firing. This product is low-fire clay that can be fired at 650 ºC/1200 ºF, and is pure silver (99.9%) after firing.
More info...
The special formula of this product allows for combination with glass,
porcelain and ceramic materials, and is also suitable for firing with
sterling silver findings or wires (SV925 and higher quality
recommended). Do not fire a soldered piece with 650/1200 Paste as the
soldering temperature is lower than the firing temperature.
[Instructions] Some silver settling may occur at the bottom of the jar.
Stir the paste well with a brush or a metal spatula before use. To
dilute the paste take out the necessary amount and place it in a
different container. (Do not dilute directly in bottle.)
This
product is water-based and can dry up. Always keep the container tightly
capped. (If it becomes too thick, add a little water and stir well)
Wash the paste off your hands with water after use. The clay may crack
during firing if it is not completely dry. Some kilns display a
different temperature from the actual inside temperature. It is known
that silver will melt at 961 ºC/1763 ºF. It is recommended that your
kiln firing temperature does not exceed 900 ºC/1652 ºF. You may combine
650/1200 Paste with the original silver clay series (clay, paste and
syringe types), but the firing conditions should be the same as the
original clay series. You may combine 650/1200 Paste with any other
650/1200 series product (clay, paste and syringe types). Do not bend the
fired piece with unreasonable pressure. Keep the clay indoors, out of
direct sunlight, and do not store in a refrigerator. For best results
use the clay as soon as possible after opening the package.
650/1200 Low Fire Silver Paste 20g
Art Clay Silver 650/1200 Paste consists of pure silver particles, a binding agent and water.
Art Clay Silver 650/1200 Paste consists of pure silver particles, a
binding agent and water. The binding agent is produced from harmless
pulp fiber. During firing, the pure silver particles solidify. The
binding agent consists of carbon, hydrogen, and oxygen resulting in the
release of harmless carbon dioxide and steam during firing. This product
is low-fire clay that can be fired at 650 ºC/1200 ºF, and is pure
silver (99.9%) after firing. The special formula of this product allows
for combination with glass, porcelain and ceramic materials, and is also
suitable for firing with sterling silver findings or wires (SV925 and
higher quality recommended). Do not fire a soldered piece with 650/1200
Paste as the soldering temperature is lower than the firing temperature.
More info...
[Instructions]
Some silver settling may occur at the bottom of the jar. Stir the paste well with a brush or a metal spatula before use. To dilute the paste take out the necessary amount and place it in a different container. (Do not dilute directly in bottle.)
This product is water-based and can dry up. Always keep the container tightly capped. (If it becomes too thick, add a little water and stir well) Wash the paste off your hands with water after use. The clay may crack during firing if it is not completely dry. Some kilns display a different temperature from the actual inside temperature. It is known that silver will melt at 961 ºC/1763 ºF. It is recommended that your kiln firing temperature does not exceed 900 ºC/1652 ºF. You may combine 650/1200 Paste with the original silver clay series (clay, paste and syringe types), but the firing conditions should be the same as the original clay series. You may combine 650/1200 Paste with any other 650/1200 series product (clay, paste and syringe types). Do not bend the fired piece with unreasonable pressure. Keep the clay indoors, out of direct sunlight, and do not store in a refrigerator. For best results use the clay as soon as possible after opening the package.